Chemical Composition (%) of 416HT Stainless Steel Plate C Mn Si P S Cr 0.15 1.25 1.00 0.06 0.15 12.0-14.0 Mechanical Properties of 416HT Stainless Steel Plate Tempering Temperature (°C) Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Brinell (HB) Impact Charpy V (J) Annealed * 517 276 30 262 […]

Chemical Composition (%) of 420 Stainless Steel Plate C Mn Si P S Cr 0.15 1.00 1.00 0.04 0.03 12.0-14.0 Mechanical Properties of 420 Stainless Steel Plate Tempering Temperature (°C) Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Brinell (HB) Annealed * 655 345 25 241 max 399°F (204°C) 1600 […]

Chemical Composition (%) of 422 Stainless Steel Plate C Mn Si Mo Ni W Cr 0.23 0.75 0.35 1.00 0.80 1.00 11.50 Mechanical Properties of 422 Stainless Steel Plate Tensile Strength MPa (min) Yield Strength 0.2% MPa(min) Elongation % Hardness (Brinell) MAX Hardness (Rockwell B) MAX 897 207 15 290 95 With better strength at […]

Grade C Mn Si P S Cr Mo Ni N 430 0.12 1.00 1.00 0.040 0.030 16.0-18.0 – 0.75 – 430F 0.12 1.25 1.00 0.06 0.15 16.0-18.0 – – – Mechanical Properties of 430 Stainless Steel Plate Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness Rockwell […]

Chemical Composition (%) of 440C Stainless Steel Plate C Mn Si Mo Ni N P S Cr 0..95-1.20 1.00 1.00 0.75 – – 0.040 0.030 16.00-18.00 Mechanical Properties of 440C Stainless Steel Plate Tempering Temperature (°C) Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Rockwell (HR C) Impact Charpy V […]

Chemical Composition (%) of NM360 Wear Resistant Steel C Si Mn P S Cr Mo Ni B ≤0.17 ≤0.50 ≤1.5 ≤0.025 ≤0.015 ≤0.70 ≤0.40 ≤0.50 ≤0.005 Mechanical Properties of NM360 Wear Resistant Steel Thickness/mm ReL /MPa Rm /MPa A/% Hardness HBW10/3000 Impact -20℃/J 20 1050 1160 19.0 360.0 65 25 1020 1180 18.5 375.0 52 […]

Chemical Composition (%) of NM400 Wear Resistant Steel C max Si max Mn max P S Cr max Mo max 0.22 2.0 2.2 ≤0.020 ≤0.006 0.90 0.50 Mechanical Properties of NM400 Wear Resistant Steel Thickness mm Yield Strength (MPa) Tensile Strength (MPa) Elongation (%) Hardness (HB) 20℃(AKV) 8-50 ≥900 ≥1150 ≥10 360-420 ≥25 Contrast Test […]

Chemical Composition (%) of NM450 Wear Resistant Steel C Si Mn P S Al Cr+Mo+Ni 0.10-0.40 0.20-0.40 1.0-2.0 ≤0.015 ≤0.003 ≥0.02 Mechanical Properties of NM450 Wear Resistant Steel Thickness/mm ReL /MPa Rm /MPa A/% Hardness/ HBW10/3000 Impact -20℃ /J 8 1250 1460 16 445 40 12 1290 1470 17 462 43 20 1370 1450 17 […]

Chemical Composition (%) of NM450 Wear Resistant Steel C Si Mn P S Cr Ni Mo Ti B ALs 0.38 0.70 1.7 0.020 0.010 1.2 1.0 0.65 0.05 0.005- 0.006 0.010 min Mechanical Properties of NM450 Wear Resistant Steel Property Impact test HBW Yield Mpa Min Tensile Mpa Elongation Min J Min 470 Thickness mm […]

About Established in 1998, Henan Anson Steel Co., Ltd or ANSON is specialized in steel plate export. As a professional and reliable steel plate supplier, we have built cooperation with over 30 countries and regions, including USA, Europe, Saudi Arabia, Egypt, Bangladesh, Sri Lanka, Korea, Vietnam, Myanmar and so on. For any steel plates we […]