Chemical Composition (%) of 410S Stainless Steel Plate
| C | Mn | Si | P | S | Cr | Ni |
| 0.08 | 1.0 | 1.0 | 0.04 | 0.03 | 11.5-14.5 | 0.60 |
Mechanical Properties of 410S Stainless Steel Plate
| Tensile Strength MPa (min) | Yield Strength 0.2% MPa(min) | Elongation (% in 50mm) min | Hardness (Rockwell B) MAX |
| 444 | 290 | 33 | 75 |
Physical Properties of 410S Stainless Steel Plate
|
Density lbm/in3 |
Thermal Conductivity (BTU/h ft. °F) |
Electrical Resistivity (in x 10-6) |
Modulus of Elasticity (psi x 106 |
Coefficient of Thermal Expansion (in/in)/ °F x 10-6 |
Specific Heat (BTU/lb/ °F) |
Melting Range (°F) |
| at 68°F: 0.280 | 187 at 212°F | 23.7 at 68°F | 29 | 6.0 at 32 – 212°F | 0.11 at 68°F to 212°F | 2700 to 2790 |
Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden.
410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. 410S is completely ferritic in the annealed condition. It exhibits adequate corrosion resistance similar to 410 and good oxidation resistance.
If you are interested in other Stainless Steel Plates/Sheets, please click 302, 303, 304, 304L, 304H, 309, 309S, 310, 310S, 310H, 316, 316L, 317/317L, 317LMN, 321, 321H, 330, 347, 347H, 904L, 403, 405, 409, 410, 410S, 410/HT, 416, 416HT, 420, 422, 430, 440C, Duplex 2205, Duplex 2304, Duplex 2507.