410S stainless steel

410S Stainless Steel Sheet for Sale

Chemical Composition (%) of 410S Stainless Steel Plate

C Mn Si P S Cr Ni
0.08 1.0 1.0 0.04 0.03 11.5-14.5 0.60

Mechanical Properties of 410S Stainless Steel Plate

Tensile Strength MPa (min) Yield Strength 0.2% MPa(min) Elongation (% in 50mm) min Hardness (Rockwell B) MAX
444 290 33 75

Physical Properties of 410S Stainless Steel Plate

Density
lbm/in3
Thermal Conductivity
(BTU/h ft. °F)
Electrical
Resistivity
(in x 10-6)
Modulus of
Elasticity
(psi x 106
Coefficient of
Thermal Expansion
(in/in)/
°F x 10-6
Specific Heat
(BTU/lb/
°F)
Melting
Range
(°F)
at 68°F: 0.280 187 at 212°F 23.7 at 68°F 29 6.0 at 32 – 212°F 0.11 at 68°F to 212°F 2700 to 2790

Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden.

410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. 410S is completely ferritic in the annealed condition. It exhibits adequate corrosion resistance similar to 410 and good oxidation resistance.

If you are interested in other Stainless Steel Plates/Sheets, please click 302, 303, 304, 304L, 304H, 309, 309S, 310, 310S, 310H, 316, 316L, 317/317L, 317LMN, 321, 321H, 330, 347, 347H, 904L, 403, 405, 409, 410, 410S, 410/HT, 416, 416HT, 420, 422, 430, 440C, Duplex 2205, Duplex 2304, Duplex 2507.

Get In touch with

Leave a Reply

Your email address will not be published. Required fields are marked *

Free Worldwide shipping

On all orders above $50

Easy 30 days returns

30 days money back guarantee

International Warranty

Offered in the country of usage

100% Secure Checkout

PayPal / MasterCard / Visa