High Strength Low Alloy Steel Plates Standard: A36, A514, A572, A588, A633, A656, SA514, SA572, SA588, SA633, SA656, EN10025-2, EN10025-3, EN10025-4, EN10025-6, JIS G3101, JIS G3106, DIN 17100, DIN 17102, GB/T700, GB/T1591, GB/T16270                                             […]

NM400 is one kind of Chinese wear/abrasion resistant steel plates, which is well received in middle east and Africa. An NM400 wear-resistant steel was hot rolled and then the plates were heat-treated by direct quenching and tempering and reheat quenching and tempering techniques, respectively. The impact test was carried out with an instrumented impact tester. […]

Alloy 304 a T-300 series stainless steel austenitic, which has a minimum of 18% chromium and 8% nickel. Type 304 has a maximum carbon of 0.07% . It is the standard “18/8 stainless” that is commonly found in pans and cooking tools. Alloy 304 is the most versatile and widely used alloy in the stainless […]

304L stainless steel plate is part of the austenitic family of stainless steel and one of the most versatile and widely used varieties of stainless plate. It is a relatively low cost stainless product and used in a variety of applications. 304 grades have excellent low temperature properties and respond well to hardening by cold […]

Alloy 304H (S30409) is a modification of the most widely utilized “18-8” chromium-nickel austenitic stainless steel. The carbon content is controlled in the range of 0.04-0.10% for increased strength at temperatures above 800°F (427°C). It is an economical and versatile corrosion resistant alloy suitable for a wide range of general purpose applications. It is common […]

309 stainless steel is an austenitic stainless steel that machines comparably to 304. However, 309 has superior corrosion resistance and strength. Cold working 309 will increase both strength and hardness and this stainless steel does not respond to heat treating. 309 is a highly alloyed stainless steel used for its excellent oxidation resistance, high temperature […]

Chemical Composition (%) of 309S and 309H Stainless Steel Plate   C Mn Si P S Cr Ni 309S max: 0.08 2.0 max 0.75 max 0.045 max 0.03 max min: 22.0 max: 24.0 min: 12.0 max: 15.0 309H min: 0.04 max: 0.10 2.0 max 0.75 max 0.045 max 0.03 max min: 22.0 max: 24.0 min: […]

Chemical Composition (%) of 310 Stainless Steel Plate Cr Ni C Si Mn P S Mo Cu 24.0 -26.0 19.0-22.0 0.25 0.75 2.0 0.045 0.030 0.75 0.5 Mechanical Properties of 310 Stainless Steel Plate Tensile Strengtd ksi (min.) Yield Strength 0.2% Offset ksi (min.) Elongation – % in 50 mm (min.) Hardness (Brinell) MAX Hardness […]

Chemical Composition (%) of 310S Stainless Steel Plate % Cr Ni C Si Mn P S Mo Cu 310S 24.0-26.0 19.0-22.0 0.08 1.00 2.0 0.045 0.030 0.75 0.5 Mechanical Properties of 310S Stainless Steel Plate Tensile Strengtd ksi (min.) Yield Strength 0.2% Offset ksi (min.) Elongation – % in 50 mm (min.) Hardness (Brinell) MAX […]

Chemical Composition (%) of 310H Stainless Steel Plate Cr Ni C Si Mn P S 24.0-26.0 19.0-22.0 0.04-0.1 0.75 2.0 0.045 0.030 Mechanical Properties of 310H Stainless Steel Plate Tensile Strengtd ksi (min.) Yield Strength 0.2% Offset ksi (min.) Elongation – % in 50 mm (min.) Hardness (Brinell) MAX Hardness (Rockwell B) MAX 75 30 […]